C3712
C3712, Engraving brass, are 60/40 alpha-beta brasses with different levels of lead added to give free machining properties. They are widely used for engraved plates and plaques, builder’s hardware, gears. They should not be used for acid etched work, for which the single-phase alpha brasses should be used.
CHEMICAL COMPOSITION
| Elements | Min (%) | Max (%) |
|---|---|---|
| Cu | 58.00 | 62.00 |
| Pb | 0.25 | 1.20 |
| Sn+Fe | - | 0.80 |
| Zn | Remainder | |
MECHANICAL PROPERTIES ACCORDING TO EN12164 (AS PER TEMPER R410)
| Range (mm) | From | To | UTS Min (MPa) | UTS Max (MPa) | PS Min (MPa) | Elongation Min (%) | Hardness Min | Hardness Max | |
|---|---|---|---|---|---|---|---|---|---|
| Round (Dia) | 6 | 75 | 315 | - | - | 15 | - | - | |
| Hex (A/F) | 6 | 70 | 70 | - | - | 15 | - | - | |
| Square (A/F) | 6 | 60 | 315 | - | - | 15 | - | - | |
| Rectangle | Thickness | 6 | 50 | 315 | - | - | 15 | - | - |
| PHYSICAL PROPERTIES | |
|---|---|
| Melting Point - Liquidus °F | 1650 |
| Melting Point - Solidus °F | 1630 |
| Density lb/cu in at 68°F | 0.304 |
| Specific Gravity | 8.41 |
| Electrical Conductivity %IACS at 68°F | 27 |
| Thermal Conductivity BTU/ sq ft/ ft hr/ °F at 68°F | 69 |
| Coefficient of Thermal Expansion 68-572 10⁻⁶ per °F (68 – 572°F) | 11.6 |
| Specific Heat BTU/ lb /°F at 68°F | 0.09 |
| Modulus of Elasticity in Tension ksi | 15000 |
| Modulus of Rigidity ksi | 5600 |
| FABRICATION PROPERTIES | |
|---|---|
| Technique | Suitability |
| Soldering | Excellent |
| Brazing | Good |
| Oxyacetylene Welding | Not Recommended |
| Gas Shielded Arc Welding | Not Recommended |
| Coated Metal Arc Welding | Not Recommended |
| Spot Welding | Not Recommended |
| Seam Welding | Not Recommended |
| Butt Welding | Fair |
| Capacity for Being Cold Worked | Fair |
| - | Excellent |
| Machinability Rating | 70 |
TYPICAL USES
- Industrial