C36300
C36300 is a lead free material suited for the use in drinking water applications. C36300 can be used where no high mechanical stresses occur. Uses: A ductile alloy suitable for blanking, riveting, bending, hot forging and pressing, hot heading, up-setting large nuts & bolts and brazing rods.
CHEMICAL COMPOSITION
| Elements | Min (%) | Max (%) |
|---|---|---|
| Cu | 61.00 | 63.00 |
| Pb | 0.25 | 0.7 |
| Fe | - | 0.15 |
| P | 0.04 | 0.15 |
| Total Others | - | 0.5 |
| Zn | Remainder | |
MECHANICAL PROPERTIES ACCORDING TO ASTM B921 (AS PER TEMPER HO2)
| Range (inch) | From | To | UTS Min (ksi) | UTS Max (ksi) | PS Min (ksi) | Elongation Min (%) | Hardness Min (HRB) | Hardness Max (HRB) | |
|---|---|---|---|---|---|---|---|---|---|
| Round (Dia) | 0.059 | 0.5 | 63 | - | 28 | 10 | - | - | |
| 0.500 | 1.000 | 55 | - | 26 | 12 | - | - | ||
| 2.000 | 2.9527 | 45 | - | 20 | 25 | - | - | ||
| Hex (A/F) | 0.1181 | 0.500 | 63 | - | 28 | 10 | - | - | |
| 0.500 | 1.000 | 55 | - | 26 | 12 | - | - | ||
| 2.000 | 2.7559 | 45 | - | 20 | 25 | - | - | ||
| Square (A/F) | 0.1181 | 0.500 | 63 | - | 28 | 10 | - | - | |
| 0.500 | 1.000 | 55 | - | 26 | 12 | - | - | ||
| 2.000 | 2.3622 | 45 | - | 20 | 25 | - | - | ||
| Rectangle | Thickness | 0.1181 | 0.500 | 63 | - | 28 | 10 | - | - |
| Thickness | 0.500 | 1.000 | 55 | - | 26 | 12 | - | - | |
| Thickness | 1.000 | 1.9685 | 48 | - | 24 | 20 | - | - | |
| Range (inch) | From | To | UTS Min (MPa) | UTS Max (MPa) | PS Min (MPa) | Elongation Min (%) | Hardness Min (HRB) | Hardness Max (HRB) | |
|---|---|---|---|---|---|---|---|---|---|
| Round (Dia) | 1.5 | 12 | 430 | - | 190 | 10 | - | - | |
| 12 | 25 | 380 | - | 180 | 12 | - | - | ||
| 25 | 50 | 330 | - | 165 | 20 | - | - | ||
| 50 | 75 | 310 | - | 135 | 25 | - | - | ||
| Hex (A/F) | 3 | 12 | 430 | - | 190 | 10 | - | - | |
| 12 | 25 | 380 | - | 180 | 12 | - | - | ||
| 25 | 50 | 330 | - | 165 | 20 | - | - | ||
| 50 | 70 | 310 | - | 135 | 25 | - | - | ||
| Square (A/F) | 3 | 12 | 430 | - | 190 | 10 | - | - | |
| 12 | 25 | 380 | - | 180 | 12 | - | - | ||
| 25 | 50 | 330 | - | 165 | 20 | - | - | ||
| 50 | 70 | 310 | - | 135 | 25 | - | - | ||
| Rectangle | Thickness | 3 | 12 | 430 | - | 190 | 10 | - | - |
| Thickness | 12 | 25 | 380 | - | 180 | 12 | - | - | |
| Thickness | 25 | 50 | 330 | - | 165 | 20 | - | - | |
| PHYSICAL PROPERTIES | |
|---|---|
| Melting Point - Liquidus°F | 1650 |
| Melting Point - Solidus°F | 1630 |
| Densitylb/cu in. at 68°F | 0.304 |
| Specific Gravity | 8.42 |
| Electrical Conductivity% IACS at 68°F | 26 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 51.5 |
| Specific Heat Capacity Btu/ lb / °F at 68 F | 0.088 |
| FABRICATION PROPERTIES | |
|---|---|
| Technique | Suitability |
| Soldering | Excellent |
| Brazing | Good |
| Oxyacetylene Welding | Fair |
| Gas Shielded Arc Welding | Fair |
| Coated Metal Arc Welding | Not Recommended |
| Spot Weld | Fair |
| Seam Weld | Not Recommended |
| Butt Weld | Fair |
| Capacity for Being Cold Worked | Excellent |
| Capacity for Being Hot Formed | Excellent |
| Forgeability Rating | Good |
| Machinability Rating | 80 |
TYPICAL USES
- Plumbing