C35330
DESCRIPTION
C35330 a dezincification-resistant machining brass, is particularly suitable for use in warm, acidic waters. This material passes the dezincification test according to ISO 6509. For the manufacture of hot-stamped parts C35330 with better hot-working properties is recommended. To achieve dezincification resistance a heat treatment may be necessary after hot working.
CHEMICAL COMPOSITION
| Elements |
Min (%) |
Max (%) |
| Cu |
59.50 |
64.00 |
| Pb |
1.50 |
3.50 |
| Fe |
- |
- |
| As |
0.02 |
0.25 |
| Total Others |
- |
0.50 |
| Zn |
Remainder |
MECHANICAL PROPERTIES ACCORDING TO ASTM B453 (AS PER TEMPER HO2)
| Range (Inch) |
From |
To |
UTS Min (ksi) |
UTS Max (ksi) |
PS Min (ksi) |
Elongation Min (%) |
Hardness Min (HRB) |
Hardness Max (HRB) |
| Round (Dia) |
0.059 |
0.500 |
57 |
80 |
25 |
7 |
60 |
80 |
| 0.500 |
1.000 |
55 |
70 |
25 |
10 |
50 |
75 |
| 1.000 |
2.953 |
50 |
62 |
20 |
15 |
40 |
70 |
| Hex (A/F) |
0.118 |
0.500 |
57 |
80 |
25 |
7 |
60 |
80 |
| 0.500 |
1.000 |
55 |
70 |
25 |
10 |
50 |
75 |
| 1.000 |
2.756 |
50 |
62 |
20 |
15 |
40 |
70 |
| Square (A/F) |
0.118 |
0.500 |
57 |
80 |
25 |
7 |
60 |
80 |
| 0.500 |
1.000 |
55 |
70 |
25 |
10 |
50 |
75 |
| 1.000 |
2.362 |
50 |
62 |
20 |
15 |
40 |
70 |
| Range (mm) |
From |
To |
UTS Min (MPa) |
UTS Max (MPa) |
PS Min (MPa) |
Elongation Min (%) |
Hardness Min (HRB) |
Hardness Max (HRB) |
| Round (Dia) |
1.5 |
12 |
395 |
555 |
170 |
7 |
60 |
80 |
| 12 |
25 |
380 |
485 |
170 |
10 |
50 |
75 |
| 25 |
75 |
345 |
425 |
140 |
15 |
40 |
70 |
| Hex (A/F) |
3 |
12 |
395 |
555 |
170 |
7 |
60 |
80 |
| 12 |
25 |
380 |
485 |
170 |
10 |
50 |
75 |
| 25 |
70 |
345 |
425 |
140 |
15 |
40 |
70 |
| Square (A/F) |
3 |
12 |
395 |
555 |
170 |
7 |
60 |
80 |
| 12 |
25 |
380 |
485 |
170 |
10 |
50 |
75 |
| 25 |
60 |
345 |
425 |
140 |
15 |
40 |
70 |
| PHYSICAL PROPERTIES |
| Melting Point - Liquidus°F |
1660 |
| Melting Point - Solidus°Fq |
1645 |
| Density lb/cu in. at 68°F |
8.45 |
| Specific Gravity |
8.45 |
| Electrical Conductivity % IACS at 68°F |
26 |
| Coefficient of Thermal Expansion 68-57210⁻⁶ per °F (68 – 572°F) |
12.4 |
| Modulus of Elasticity in Tension ksi |
15000 |
| FABRICATION PROPERTIES |
No Fabrication properties for this alloy. |
TYPICAL USES